The product has been finished with a matte coating. The specific surface finish of the material allows for the application of post-processing techniques. It is recommended that prints are made using an ABS, heated bed or enclosed chamber. Weight: 1.00 kg.
No support file available
| SUGGESTED PRINT SETS (1) |
| Suggested print sets | unit | value | test method |
| extruder temp | C° | 235-250 | internal |
| plate temp | C° | 90 | internal |
| min. nozzle diameter | mm | 0,2 | internal |
| fan | % | 0-70 | internal |
| print speed | mm/1° | 30-60 | internal |
| PROPERTY |
| Physical | | | |
| Specific gravity | g/cm3 | 1.06 | ISO 1183 |
| Mechanical | | | |
| Tensile strength yield | MPa | 46 | ISO 527 |
| Tensile strength break | MPa | 34 | ISO 527 |
| Tensile elongation | % | 31 | ISO 527 |
| Charpy impact (23°C) | kJ/m2 | 20 | ISO 179 |
| Flexural strength | MPa | 76 | ISO 178 |
| Flexural modulus | GPa | 2.2 | ISO 178 |
| Izod impact strength (23°C) | kJ/m2 | 19 | ISO 180/1A |
| Izod impact strength (-30°C) | kJ/m2 | 9 | ISO 180/1A |
| Thermal | | | |
| Heat distortion temp. (unannealed) | °C | 83 | ISO 75 A |
| Heat distortion temp. (annealed) | °C | 98 | ISO 75 A |
| Coefficient of linear thermal expansion | - | 8.6 x 10-5 | 8.6 x 10-5 |
| Flammability | - | 1.5 mm HB | UL 94 |
| Mold shrinkage | % | 0.4-0.7 | ISO 294-4 |
| Vicat softening temp. | °C | 104 | ISO 306 |