The optimal applications for this product include use in circulation pumps, body and turbine components that come into contact with aggressive fluids, making it suitable for ATEX-certified environments. Additionally, it is well-suited for use in automotive engine components and railway communications cases. It is not necessary to pre-dry this material, as hygroscopy will not disturb it. Weight: 0.75 kg.
| SUGGESTED PRINT SETS (1) |
| Suggested print sets | unit | value | test method |
| extruder temp | C° | 255-270 | internal |
| plate temp | C° | 50 | internal |
| min. nozzle diameter (2) | mm | 0,5 | internal |
| fan | % | 0 | internal |
| print speed | mm/1° | 35-45 | internal |
| PROPERTY |
| Physical | | | |
| Specific gravity | g/cm3 | 1 | ISO 1183 |
| Water absorption | % | <0,3 | 23°C / 24 h |
| Linear mould shrinkage | % | 0,2-0,6 | DIN 16901 |
| Mechanical at 23°C / 50% rh | | | |
| Tensile strength | MPa | 54 | ISO 527 |
| Elongation at maximum force | % | 1,2 | ISO 527 |
| Modulus of elasticity | GPa | 7 | ISO 527 |
| Flexural strength | MPa | 78 | ISO 178 |
| Flexural modulus | GPa | 6 | ISO 178 |
| Flexural elongation | % | 1,5 | ISO 178 |
| Charpy impact strength | kJ / m2 | 35 | ISO 179 1eU |
| Thermal | | | |
| Vicat softening temp | °C | 80 | DIN ISO 306 |
| Continuous service temp. | °C | 100 | UL 746B |
| Maximum (short term) use temp. | °C | 130 | - |
| Electrical | | | |
| Insulation resistance | Ω | ≤103 -7 | DIN/IEC 60167 |
| Surface resistance | Ω | <107 | DIN IEC 60093 |